06Cr13Al — stainless Steel: Composition, Properties & Applications
Also known as: 06Cr13Al
Al-stabilized ferritic, weldable. (GB/T 20878; equiv ASTM 405 / EN 1.4002 / JIS SUS405). Nominal values—confirm mill certificate.
CHEMICAL COMPOSITION
C:≤0.08;Cr:11.5-14.5;Al:0.10-0.30
MECHANICAL PROPERTIES
Tensile:≥415 MPa;Yield:≥170 MPa
TYPICAL APPLICATIONS
铝稳定铁素体，可焊。,"Sheet
AVAILABLE FORMS
Bar"
STANDARDS & EQUIVALENT GRADES
T 20878 06Cr13Al; ASTM 405; EN 1.4002 / JIS SUS405
HEAT TREATMENT
Annealed at 780–850 °C and air cooled; stabilize at 600–800 °C to avoid 475 °C embrittlement; not hardenable by heat treatment.
PROCESSING PRECAUTIONS
Avoid welding in the 475 °C embrittlement and sigma-phase ranges; use matched filler and minimize heat input. Good resistance to stress-corrosion cracking.
SOURCE & SUPPLY
Shanxi Youte Steel stocks 06Cr13Al in bars, plates, pipes and forgings with mill test certificates, cut-to-length service and export packaging. Contact our team for quotations and technical data sheets.
Al-stabilized ferritic, weldable. (GB/T 20878; equiv ASTM 405 / EN 1.4002 / JIS SUS405). Nominal values—confirm mill certificate.
CHEMICAL COMPOSITION
C:≤0.08;Cr:11.5-14.5;Al:0.10-0.30
MECHANICAL PROPERTIES
Tensile:≥415 MPa;Yield:≥170 MPa
TYPICAL APPLICATIONS
铝稳定铁素体，可焊。,"Sheet
AVAILABLE FORMS
Bar"
STANDARDS & EQUIVALENT GRADES
T 20878 06Cr13Al; ASTM 405; EN 1.4002 / JIS SUS405
HEAT TREATMENT
Annealed at 780–850 °C and air cooled; stabilize at 600–800 °C to avoid 475 °C embrittlement; not hardenable by heat treatment.
PROCESSING PRECAUTIONS
Avoid welding in the 475 °C embrittlement and sigma-phase ranges; use matched filler and minimize heat input. Good resistance to stress-corrosion cracking.
SOURCE & SUPPLY
Shanxi Youte Steel stocks 06Cr13Al in bars, plates, pipes and forgings with mill test certificates, cut-to-length service and export packaging. Contact our team for quotations and technical data sheets.