06Cr13Si4Nb — stainless Steel: Composition, Properties & Applications
Also known as: 06Cr13Si4Nb
General-purpose ferritic stainless steel. (GB/T 20878; equiv ASTM 430 / EN 1.4016 / JIS SUS430 / GB 10Cr17). Nominal values—confirm mill certificate.
CHEMICAL COMPOSITION
C:≤0.12;Cr:16.0-18.0;Mn:≤1.00
MECHANICAL PROPERTIES
Tensile:≥450 MPa;Yield:≥205 MPa;Elong:≥22%
TYPICAL APPLICATIONS
通用铁素体不锈钢。,"Sheet
AVAILABLE FORMS
Bar
STANDARDS & EQUIVALENT GRADES
T 20878 06Cr13Si4Nb; ASTM 430; Preheat and post-weld heat treat to avoid hydrogen cracking; soft anneal before heavy machining. Lower corrosion resistance than austenitic grades — not for strong chlorides.
HEAT TREATMENT
Martensitic stainless steel combining moderate corrosion resistance with high strength and hardness after heat treatment. Used for cutlery, surgical instruments, turbine blades, valves, pumps, fasteners and bearings in mildly corrosive environments.
PROCESSING PRECAUTIONS
Annealing/quench from 980–1050 °C (oil or air) then temper 150–650 °C; lower temper gives higher hardness, higher temper improves toughness.
SOURCE & SUPPLY
Shanxi Youte Steel stocks 06Cr13Si4Nb in bars, plates, pipes and forgings with mill test certificates, cut-to-length service and export packaging. Contact our team for quotations and technical data sheets.
General-purpose ferritic stainless steel. (GB/T 20878; equiv ASTM 430 / EN 1.4016 / JIS SUS430 / GB 10Cr17). Nominal values—confirm mill certificate.
CHEMICAL COMPOSITION
C:≤0.12;Cr:16.0-18.0;Mn:≤1.00
MECHANICAL PROPERTIES
Tensile:≥450 MPa;Yield:≥205 MPa;Elong:≥22%
TYPICAL APPLICATIONS
通用铁素体不锈钢。,"Sheet
AVAILABLE FORMS
Bar
STANDARDS & EQUIVALENT GRADES
T 20878 06Cr13Si4Nb; ASTM 430; Preheat and post-weld heat treat to avoid hydrogen cracking; soft anneal before heavy machining. Lower corrosion resistance than austenitic grades — not for strong chlorides.
HEAT TREATMENT
Martensitic stainless steel combining moderate corrosion resistance with high strength and hardness after heat treatment. Used for cutlery, surgical instruments, turbine blades, valves, pumps, fasteners and bearings in mildly corrosive environments.
PROCESSING PRECAUTIONS
Annealing/quench from 980–1050 °C (oil or air) then temper 150–650 °C; lower temper gives higher hardness, higher temper improves toughness.
SOURCE & SUPPLY
Shanxi Youte Steel stocks 06Cr13Si4Nb in bars, plates, pipes and forgings with mill test certificates, cut-to-length service and export packaging. Contact our team for quotations and technical data sheets.