X850
X8501-H32 · aluminum
X8501-H32
Sheet,Plate,Extrusion | AA X8501
Si:0.40-0.80;Fe:≤0.70;Cu:0.15-0.40;Mn:≤0.15;Mg:0.80-1.20;Cr:0.04-0.35;Zn:≤0.25;Ti:≤0.15
X850
X8501-H34 · aluminum
X8501-H34
Sheet,Plate,Extrusion | AA X8501
Si:0.40-0.80;Fe:≤0.70;Cu:0.15-0.40;Mn:≤0.15;Mg:0.80-1.20;Cr:0.04-0.35;Zn:≤0.25;Ti:≤0.15
X850
X8501-H36 · aluminum
X8501-H36
Sheet,Plate,Extrusion | AA X8501
Si:0.40-0.80;Fe:≤0.70;Cu:0.15-0.40;Mn:≤0.15;Mg:0.80-1.20;Cr:0.04-0.35;Zn:≤0.25;Ti:≤0.15
X850
X8501-H38 · aluminum
X8501-H38
Sheet,Plate,Extrusion | AA X8501
Si:0.40-0.80;Fe:≤0.70;Cu:0.15-0.40;Mn:≤0.15;Mg:0.80-1.20;Cr:0.04-0.35;Zn:≤0.25;Ti:≤0.15
X850
X8501-O · aluminum
X8501-O
Sheet,Plate,Extrusion | AA X8501
Si:0.40-0.80;Fe:≤0.70;Cu:0.15-0.40;Mn:≤0.15;Mg:0.80-1.20;Cr:0.04-0.35;Zn:≤0.25;Ti:≤0.15
X8Cr
X8Cr17 · stainless
X8Cr17
Bar | DIN 17440 X8Cr17
C:≤0.12;Cr:16.0-18.0;Mn:≤1.00
X8Cr
X8CrMoTi17 · alloy
X8CrMoTi17
Bar,Plate | DIN 17240 X8CrMoTi17
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
X8Cr
X8CrNb17 · alloy
X8CrNb17
Bar,Plate | DIN 17240 X8CrNb17
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
X8Cr
X8CrNi 25-21 · other
X8CrNi 25-21 / 1.4845
Bar, Plate, Tube, Forging |
C:≤0.1;Si:≤1.5;Mn:≤2;P:≤0.045;S:≤0.015;Cr:24-26;Ni:19-22;N:≤0.11
X8Cr
X8CrNi25-21 · stainless
X8CrNi25-21
Bar" | DIN 17240 X8CrNi25-21
C:≤0.08;Cr:24.0-26.0;Ni:19.0-22.0
X8Cr
X8CrNiMoNb16-16 · stainless
X8CrNiMoNb16-16
Bar" | DIN 17240 X8CrNiMoNb16-16
C:≤0.08;Cr:24.0-26.0;Ni:19.0-22.0
X8Cr
X8CrNiNb16-13 · stainless
X8CrNiNb16-13
Bar" | DIN 17240 X8CrNiNb16-13
C:≤0.08;Cr:24.0-26.0;Ni:19.0-22.0
X8Cr
X8CrNiSi20-12 · stainless
X8CrNiSi20-12
Bar" | DIN 17240 X8CrNiSi20-12
C:≤0.08;Cr:24.0-26.0;Ni:19.0-22.0
X8Cr
X8CrTi17 · alloy
X8CrTi17
Bar,Plate | DIN 17240 X8CrTi17
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
X8Ni
X8Ni9 · alloy
X8Ni9
Bar,Plate | EN 10028-4 X8Ni9
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
X8Ni
X8NiCrAlTi 32-21 · other
X8NiCrAlTi 32-21 / 1.4959
Bar, Plate, Tube, Forging |
C:0.05-0.1;Si:≤0.7;Mn:≤1.5;P:≤0.015;S:≤0.01;Cr:19-22;Ni:30-34;Cu:≤0.5
X8Ni
X8NiCrAlTi32-20 · stainless
X8NiCrAlTi32-20
Bar" | DIN 17240 X8NiCrAlTi32-20
C:≤0.08;Cr:24.0-26.0;Ni:19.0-22.0
X8Ni
X8NiCrAlTi32-21 · stainless
X8NiCrAlTi32-21
Bar" | DIN 17240 X8NiCrAlTi32-21
C:≤0.08;Cr:24.0-26.0;Ni:19.0-22.0
X9
X9 · other
X9
Block" | GOST 1435 X9
C:2.00-2.30;Si:≤0.40;Mn:≤0.40;Cr:11.5-13.0
X90
X90 · alloy
X90
Carburizing (case-hardening) steel with low carbon core for toughness and a hard, wear-resistant surface after carburizing. Used for gears, camshafts, pinions, spline shafts, bushings and transmission parts subjected to fatigue and surface wear. |
C:≤0.22;Mn:≤1.20;P:≤0.030;S:≤0.030