3485
3485 · alloy
3485
Bar,Plate |
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
348H
348H · stainless
348H
Sheet | ASTM A479 348H
C:≤0.08;Cr:16.0-18.0;Ni:10.0-14.0;Mo:2.00-3.00
34Cr
34Cr13Ni4Mo · stainless
34Cr13Ni4Mo
| GJB 30A GB/T 15007
C 0.31-0.37 Si ≤0.80 Mn ≤1.00 P ≤0.030 S ≤0.020 Cr 13 Ni 4 Mo 0.50-1.00 (nominal)
34Cr
34Cr18Ni3Mo · stainless
34Cr18Ni3Mo
| GJB 30A GB/T 15007
C 0.31-0.37 Si ≤0.80 Mn ≤1.00 P ≤0.030 S ≤0.020 Cr 18 Ni 3 Mo 0.50-1.00 (nominal)
34Cr
34Cr20Ni3Mo · stainless
34Cr20Ni3Mo
| GJB 30A GB/T 15007
C 0.31-0.37 Si ≤0.80 Mn ≤1.00 P ≤0.030 S ≤0.020 Cr 20 Ni 3 Mo 0.50-1.00 (nominal)
34Cr
34Cr25Ni4Mo · stainless
34Cr25Ni4Mo
| GJB 30A GB/T 15007
C 0.31-0.37 Si ≤0.80 Mn ≤1.00 P ≤0.030 S ≤0.020 Cr 25 Ni 4 Mo 0.50-1.00 (nominal)
34Cr
34Cr28Ni4Mo · stainless
34Cr28Ni4Mo
| GJB 30A GB/T 15007
C 0.31-0.37 Si ≤0.80 Mn ≤1.00 P ≤0.030 S ≤0.020 Cr 28 Ni 4 Mo 0.50-1.00 (nominal)
34Cr
34Cr2Ni2Mo · alloy
34Cr2Ni2Mo
Forging" | T 3077 34Cr2Ni2Mo
C:0.38-0.43;Si:0.15-0.35;Mn:0.60-0.80;Ni:1.65-2.00;Cr:0.70-0.90;Mo:0.20-0.30
34Cr
34Cr4 · alloy
34Cr4
Carburizing (case-hardening) steel with low carbon core for toughness and a hard, wear-resistant surface after carburizing. Used for gears, camshafts, pinions, spline shafts, bushings and transmission parts subjected to fatigue and surface wear. | DIN 17200 34Cr4, GB/T 3077 GB/T 15007
C:0.14-0.19;Mn:1.00-1.30;Cr:0.80-1.10
34Cr
34CrAlMo5 · alloy
34CrAlMo5
Forging" | DIN 17211 34CrAlMo5
C:0.35-0.42;Cr:1.35-1.65;Mo:0.15-0.25;Al:0.70-1.10
34Cr
34CrAlNi7 · alloy
34CrAlNi7
Forging" | DIN 17211 34CrAlNi7
C:0.35-0.42;Cr:1.35-1.65;Mo:0.15-0.25;Al:0.70-1.10
34Cr
34CrAlNi7-10 · alloy
34CrAlNi7-10
Bar, Forging | ~AISI 6470E mod
C:0.30-0.37;Si:≤0.40;Mn:0.40-0.70;Ni:0.80-1.10;Cr:1.50-1.80;Mo:0.15-0.25;Al:0.80-1.10
34Cr
34CrAlS5 · alloy
34CrAlS5
Forging" | DIN 17211 34CrAlS5
C:0.35-0.42;Cr:1.35-1.65;Mo:0.15-0.25;Al:0.70-1.10
34Cr
34CrMo4 · alloy
34CrMo4
Bar,Plate | EN 10277 34CrMo4, GB/T 3077 GB/T 15007
C:0.30-0.37;Si:0.15-0.40;Mn:0.60-0.90;Cr:0.90-1.20;Mo:0.15-0.30;P:≤0.035;S:≤0.035
34Cr
34CrMoS4 · alloy
34CrMoS4
Bar,Plate | EN 10277 34CrMoS4
C:0.31-0.38;Cr:0.7-1.1;Mo:0.7-1.1;P:≤0.035;S:≤0.035
34Cr
34CrNi1Mo · alloy
34CrNi1Mo
Forging" | T 3077 34CrNi1Mo
C:0.38-0.43;Si:0.15-0.35;Mn:0.60-0.80;Ni:1.65-2.00;Cr:0.70-0.90;Mo:0.20-0.30
34Cr
34CrNi1Mo6 · alloy
34CrNi1Mo6
Typically normalized (880–920 °C, air cool) or carburized (900–930 °C) for case-hardening grades, then quenched and tempered at 150–200 °C. | T 2666 34CrNi1Mo6
C:0.22-0.28;Cr:1.50-2.00;Ni:3.20-4.00;Mo:0.30-0.50;V:0.05-0.12
34Cr
34CrNi1MoA · alloy
34CrNi1MoA
Forging" | T 3077 34CrNi1MoA
C:0.38-0.43;Si:0.15-0.35;Mn:0.60-0.80;Ni:1.65-2.00;Cr:0.70-0.90;Mo:0.20-0.30
34Cr
34CrNi2Mo · alloy
34CrNi2Mo
Forging" | T 3077 34CrNi2Mo
C:0.38-0.43;Si:0.15-0.35;Mn:0.60-0.80;Ni:1.65-2.00;Cr:0.70-0.90;Mo:0.20-0.30