SUH3
SUH31 · alloy
SUH31
Bar,Plate | JIS G4901 SUH31
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
SUH3
SUH310 · alloy
SUH310
Bar,Plate | JIS G4901 SUH310
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
SUH3
SUH310J1 · stainless
SUH310J1
Bar" | JIS G4903 SUH310J1
C:≤0.08;Cr:22.0-24.0;Ni:12.0-15.0
SUH3
SUH330 · alloy
SUH330
Bar,Plate | JIS G4901 SUH330
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
SUH3
SUH330B · stainless
SUH330B
Bar" | JIS G4903 SUH330B
C:≤0.08;Cr:22.0-24.0;Ni:12.0-15.0
SUH3
SUH331 · stainless
SUH331
Bar" | JIS G4901 SUH331
C:≤0.08;Cr:24.0-26.0;Ni:19.0-22.0
SUH3
SUH340B · stainless
SUH340B
Bar" | JIS G4903 SUH340B
C:≤0.08;Cr:22.0-24.0;Ni:12.0-15.0
SUH3
SUH35 · alloy
SUH35
Bar,Plate | JIS G4901 SUH35
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
SUH3
SUH36 · alloy
SUH36
Bar,Plate | JIS G4901 SUH36
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
SUH3
SUH37 · alloy
SUH37
Bar,Plate | JIS G4901 SUH37
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
SUH3
SUH38 · alloy
SUH38
Bar,Plate | JIS G4901 SUH38
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
SUH3
SUH39 · stainless
SUH39
Bar" | JIS G4901 SUH39
C:≤0.08;Cr:24.0-26.0;Ni:19.0-22.0
SUH3
SUH3A · stainless
SUH3A
Martensitic stainless steel combining moderate corrosion resistance with high strength and hardness after heat treatment. Used for cutlery, surgical instruments, turbine blades, valves, pumps, fasteners and bearings in mildly corrosive environments. | JIS G4901 SUH3A
C:0.60-0.75;Cr:16.0-18.0
SUH4
SUH4 · stainless
SUH4
Martensitic stainless steel combining moderate corrosion resistance with high strength and hardness after heat treatment. Used for cutlery, surgical instruments, turbine blades, valves, pumps, fasteners and bearings in mildly corrosive environments. | JIS G4901 SUH4
C:0.60-0.75;Cr:16.0-18.0
SUH4
SUH4A · stainless
SUH4A
Martensitic stainless steel combining moderate corrosion resistance with high strength and hardness after heat treatment. Used for cutlery, surgical instruments, turbine blades, valves, pumps, fasteners and bearings in mildly corrosive environments. | JIS G4901 SUH4A
C:0.60-0.75;Cr:16.0-18.0
SUH5
SUH508 · alloy
SUH508
Bar,Plate | JIS G4901 SUH508
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
SUH6
SUH660 · alloy
SUH660
Bar,Plate | JIS G4901 SUH660
Ni:24.0-27.0;Cr:13.5-16.0;Ti:1.90-2.35;Mo:1.00-1.50;V:0.10-0.50;Al:≤0.35;B:0.001-0.010;C:≤0.08;Si:≤1.00;Mn:≤2.00;P:≤0.040;S:≤0.030;Fe:bal
SUH6
SUH661 · alloy
SUH661
Bar,Plate | JIS G4902 SUH661
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
SUH6
SUH662 · alloy
SUH662
Bar,Plate | JIS G4901 SUH662
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040