X5Ni
X5NiCrAlTi 31-20 · other
X5NiCrAlTi 31-20 / 1.4958
Bar, Plate, Tube, Forging |
C:0.03-0.08;Si:≤0.7;Mn:≤1.5;P:≤0.015;S:≤0.01;Cr:19-22;Ni:30-32.5;Cu:≤0.5
X60
X60 · alloy
X60
Carburizing (case-hardening) steel with low carbon core for toughness and a hard, wear-resistant surface after carburizing. Used for gears, camshafts, pinions, spline shafts, bushings and transmission parts subjected to fatigue and surface wear. |
C:≤0.22;Mn:≤1.20;P:≤0.030;S:≤0.030
X60M
X60M · alloy
X60M
Bar,Plate |
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
X60Q
X60Q · alloy
X60Q
Bar,Plate |
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
X65
X65 · alloy
X65
Carburizing (case-hardening) steel with low carbon core for toughness and a hard, wear-resistant surface after carburizing. Used for gears, camshafts, pinions, spline shafts, bushings and transmission parts subjected to fatigue and surface wear. |
C:≤0.22;Mn:≤1.20;P:≤0.030;S:≤0.030
X65M
X65M · alloy
X65M
Bar,Plate |
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
X65Q
X65Q · alloy
X65Q
Bar,Plate |
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
X6Cr
X6Cr13 · stainless
X6Cr13
Sheet,Bar | EN 10088
C:≤0.08;Si:≤1.00;Mn:≤2.00;Cr:16.0-18.0;Ni:10.0-14.0;Mo:2.0-3.0;P:≤0.045;S:≤0.030
X6Cr
X6Cr17 · stainless
X6Cr17
Bar | DIN 17440 X6Cr17
C:≤0.12;Cr:16.0-18.0;Mn:≤1.00
X6Cr
X6CrMo17 · stainless
X6CrMo17
Bar" | DIN 17440 X6CrMo17
C:≤0.12;Cr:16.0-18.0;Mo:0.75-1.25
X6Cr
X6CrNi18-10 · stainless
X6CrNi18-10
Sheet | DIN 17440 X6CrNi18-10
C:≤0.08;Si:≤1.00;Mn:≤2.00;Cr:18.0-20.0;Ni:8.0-10.5
X6Cr
X6CrNi23-13 · stainless
X6CrNi23-13
Bar" | DIN 17240 X6CrNi23-13
C:≤0.08;Cr:24.0-26.0;Ni:19.0-22.0
X6Cr
X6CrNi25-20 · stainless
X6CrNi25-20
Bar" | DIN 17240 X6CrNi25-20
C:≤0.08;Cr:24.0-26.0;Ni:19.0-22.0
X6Cr
X6CrNiMoNb17-12-2 · stainless
X6CrNiMoNb17-12-2
Sheet,Bar | EN 10088
C:≤0.08;Si:≤1.00;Mn:≤2.00;Cr:16.0-18.0;Ni:10.0-14.0;Mo:2.0-3.0;P:≤0.045;S:≤0.030
X6Cr
X6CrNiMoTi 17-12-2 · other
X6CrNiMoTi 17-12-2 / 1.4571
Bar, Plate, Tube, Forging |
C:≤0.08;Si:≤1;Mn:≤2;P:≤0.045;S:≤0.015;Cr:16.5-18.5;Ni:10.5-13.5;Mo:2-2.5
X6Cr
X6CrNiMoTi17-12-2 · alloy
X6CrNiMoTi17-12-2
Bar,Plate | EN 1092-1 X6CrNiMoTi17-12-2
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
X6Cr
X6CrNiNb 18-10 · other
X6CrNiNb 18-10 / 1.4550
Bar, Plate, Tube, Forging |
C:≤0.08;Si:≤1;Mn:≤2;P:≤0.045;S:≤0.015;Cr:17-19;Ni:9-12
X6Cr
X6CrNiNb12 · stainless
X6CrNiNb12
Bar | DIN 17440 X6CrNiNb12
C:≤0.08;Cr:17.0-19.0;Ni:9.0-13.0;Nb:≥10×C
X6Cr
X6CrNiNb18-10 · alloy
X6CrNiNb18-10
Bar,Plate | ISO 683-13 X6CrNiNb18-10
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040