06Cr13Al
Stainless Steel06Cr13Al
Al-stabilized ferritic, weldable. (GB/T 20878; equiv ASTM 405 / EN 1.4002 / JIS SUS405). Nominal values—confirm mill certificate.
Chemical Composition (%)
| C | 0.08 |
|---|---|
| CR | 11.5 |
| AL | 0.1 |
Mechanical Properties
Tensile:≥415 MPa;Yield:≥170 MPa
Chinese Standard
T 20878 06Cr13Al
Equivalent Standards
ASTM 405
Equivalent Grades
EN 1.4002 / JIS SUS405
Applications
铝稳定铁素体，可焊。,"Sheet
Available Forms
Bar"
Uses
Ferritic stainless steel with good resistance to stress-corrosion cracking and oxidation, plus formability and lower cost. Used for automotive trim, exhaust systems, domestic appliances, decorative and welded structures.
Heat Treatment
Annealed at 780–850 °C and air cooled; stabilize at 600–800 °C to avoid 475 °C embrittlement; not hardenable by heat treatment.
Precautions
Avoid welding in the 475 °C embrittlement and sigma-phase ranges; use matched filler and minimize heat input. Good resistance to stress-corrosion cracking.