08X4H2M

Alloy Steel

08X4H2M

Cr-Mo quench & temper steel. (GOST 4543; equiv GB 35CrMo / DIN 34CrMo4 / JIS SCM435). Nominal values—confirm mill certificate.

Chemical Composition (%)

C0.33
MN0.7
CR0.8
MO0.15

Mechanical Properties

Tensile:≥980 MPa;Yield:≥835 MPa

Chinese Standard

GOST 4543 08X4H2M

Equivalent Grades

GB 35CrMo / DIN 34CrMo4 / JIS SCM435

Applications

铬钼调质钢。,"Bar

Available Forms

Forging"

Uses

Low-alloy engineering steel with enhanced hardenability and strength from alloying elements. Chromium (≈0.95%) improves hardenability, wear and corrosion resistance. Molybdenum (≈0.2%) raises high-temperature strength and prevents temper embrittlement. Applied to gears, shafts, bolts, connecting rods, pressure parts and heavy forgings in automotive, energy and machinery sectors.

Heat Treatment

Austenitize at 820–870 °C (oil or water quench depending on section) and temper at 400–650 °C to the required strength/toughness balance.

Precautions

Preheat and control interpass temperature when welding; post-weld heat treatment or stress relief is recommended to avoid hard-zone cracking. Use low-hydrogen electrodes. Protect from decarburization during heating (controlled atmosphere or protective coating).