09MnNDRE

Alloy Steel

09MnNDRE

Low-temp pressure vessel steel (-70°C). (GB/T 3531; equiv GB/T 713 09MnNiDR / A203 GrE mod). Nominal values—confirm mill certificate.

Chemical Composition (%)

C0.12
MN1.2
NI0.3
P0.02
S0.01

Mechanical Properties

Tensile:440-590 MPa;Yield:≥280 MPa

Chinese Standard

T 3531 09MnNDRE

Equivalent Standards

T 713 09MnNiDR / A203 GrE mod

Applications

低温压力容器（-70℃）。,Plate

Available Forms

Carburizing (case-hardening) steel with low carbon core for toughness and a hard, wear-resistant surface after carburizing. Used for gears, camshafts, pinions, spline shafts, bushings and transmission parts subjected to fatigue and surface wear.

Uses

Typically normalized (880–920 °C, air cool) or carburized (900–930 °C) for case-hardening grades, then quenched and tempered at 150–200 °C. Carburize 900–930 °C, direct/intake quench, temper 150–200 °C; useful case depth 0.5–1.5 mm.

Heat Treatment

Weldable with standard procedures; preheat may be needed for thick sections or higher-carbon/ alloy grades. Protect from decarburization during heating (controlled atmosphere or protective coating). Machine the core stock before surface hardening; leave grinding allowance for the hardened case.