1.0577
Alloy Steel1.0577
1.0577 supplied by Shanxi Youte Steel (jlhsteel.net).
Chemical Composition (%)
| C | 0.2 |
|---|---|
| MN | 1.6 |
| SI | 0.55 |
Chinese Standard
EN 10025
Equivalent Grades
S355J2
Available Forms
Bar, Plate, Tube, Forging, Wire
Uses
Carburizing (case-hardening) steel with low carbon core for toughness and a hard, wear-resistant surface after carburizing. Used for gears, camshafts, pinions, spline shafts, bushings and transmission parts subjected to fatigue and surface wear.
Heat Treatment
Typically normalized (880–920 °C, air cool) or carburized (900–930 °C) for case-hardening grades, then quenched and tempered at 150–200 °C. Carburize 900–930 °C, direct/intake quench, temper 150–200 °C; useful case depth 0.5–1.5 mm.
Precautions
Weldable with standard procedures; preheat may be needed for thick sections or higher-carbon/ alloy grades. Protect from decarburization during heating (controlled atmosphere or protective coating). Machine the core stock before surface hardening; leave grinding allowance for the hardened case.