1.2714
Alloy Steel1.2714
(DIN 17007). Nominal values—confirm mill certificate.
Chemical Composition (%)
| C | 0.52 |
|---|---|
| SI | 0.1 |
| MN | 0.65 |
| CR | 1 |
| MO | 0.45 |
| NI | 1.5 |
| V | 0.07 |
| P | 0.03 |
| S | 0.03 |
Mechanical Properties
Hardness(annealed):≤241 HB;Hardness(hardened):42-48 HRC
Chinese Standard
DIN 17007 1.2714
Available Forms
Bar,Plate
Uses
Spring steel with high elastic limit and fatigue strength for coils, leaf springs, clips and suspension parts. Silicon (≈0.25%) raises elastic limit and tempering resistance. Supplied as strip, wire and bar; shot-peened after forming for longer service life.
Heat Treatment
Austenitize 830–880 °C (oil quench) and temper at 400–520 °C; stress-relieve formed springs at 230–320 °C after coiling.
Precautions
Preheat and control interpass temperature when welding; post-weld heat treatment or stress relief is recommended to avoid hard-zone cracking. Use low-hydrogen electrodes. Protect from decarburization during heating (controlled atmosphere or protective coating). Shot-peen after coiling to improve fatigue life; avoid sharp bends and surface defects.