11CrMo9-10

Alloy Steel

11CrMo9-10

(EN 1092-1). Nominal values—confirm mill certificate.

Chemical Composition (%)

C0.08
CR0.7
MO0.9
P0.035
S0.035

Mechanical Properties

Tensile:≥510 MPa;Yield:≥295 MPa;Elong:≥20%

Chinese Standard

EN 1092-1 11CrMo9-10

Available Forms

Bar,Plate

Uses

Tool and die steel for cutting, forming, punching and molding tools. Tungsten/molybdenum (≈0%/9.05%) give hot hardness and red-hardness for high-speed and hot-work tools. High chromium (≈0.9%) provides wear resistance and secondary hardening. Applied to blanks, punches, extrusion dies, shear blades, plastic-mold and cold-work tooling.

Heat Treatment

Powder/HSS: preheat 800–850 °C, austenitize 1180–1230 °C (salt or vacuum), quench, triple temper 540–570 °C to ≈64–66 HRC.

Precautions

Risk of quench cracking and distortion — use graded preheating, controlled cooling and multiple tempers. Avoid overheating the austenitizing temperature. Machine in the soft annealed condition; allow for dimensional change after heat treatment. Grind with coolant to prevent rehardening cracks.