12Cr2Ni4

Alloy Steel

12Cr2Ni4

High-Ni carburizing steel. (GB/T 3077; equiv GB 12Cr2Ni4 / AISI E3310). Nominal values—confirm mill certificate.

Chemical Composition (%)

C0.08
NI3.25
CR1.35

Mechanical Properties

Tensile:≥1080 MPa;Yield:≥835 MPa

Chinese Standard

T 3077 12Cr2Ni4

Equivalent Standards

AISI E3310

Applications

高镍渗碳钢。,Bar

Available Forms

Carburizing (case-hardening) steel with low carbon core for toughness and a hard, wear-resistant surface after carburizing. Used for gears, camshafts, pinions, spline shafts, bushings and transmission parts subjected to fatigue and surface wear.

Uses

Typically normalized (880–920 °C, air cool) or carburized (900–930 °C) for case-hardening grades, then quenched and tempered at 150–200 °C. Carburize 900–930 °C, direct/intake quench, temper 150–200 °C; useful case depth 0.5–1.5 mm.

Heat Treatment

Weldable with standard procedures; preheat may be needed for thick sections or higher-carbon/ alloy grades. Protect from decarburization during heating (controlled atmosphere or protective coating). Machine the core stock before surface hardening; leave grinding allowance for the hardened case.