14NiCrMo13-4
Alloy Steel14NiCrMo13-4
High-nickel case-hardening steel (DIN).
Chemical Composition (%)
| C | 0.1 |
|---|---|
| SI | 0.4 |
| MN | 0.4 |
| NI | 3.2 |
| CR | 1.2 |
| MO | 0.15 |
Mechanical Properties
Tensile Strength:≥1180 MPa;Yield Strength:≥885 MPa;Elongation:≥9%
Equivalent Standards
—,"Heavy carburized gears
Equivalent Grades
DIN 14NiCrMo13-4 / EN 1.6657
Applications
aircraft parts."
Available Forms
Bar, Forging
Uses
Carburizing (case-hardening) steel with low carbon core for toughness and a hard, wear-resistant surface after carburizing. Used for gears, camshafts, pinions, spline shafts, bushings and transmission parts subjected to fatigue and surface wear.
Heat Treatment
Typically normalized (880–920 °C, air cool) or carburized (900–930 °C) for case-hardening grades, then quenched and tempered at 150–200 °C. Carburize 900–930 °C, direct/intake quench, temper 150–200 °C; useful case depth 0.5–1.5 mm.
Precautions
Weldable with standard procedures; preheat may be needed for thick sections or higher-carbon/ alloy grades. Protect from decarburization during heating (controlled atmosphere or protective coating). Machine the core stock before surface hardening; leave grinding allowance for the hardened case.