18CrNiMo5

Alloy Steel

18CrNiMo5

Specialty steel grade. ; equiv 18CrNiMo5 / 1.6523). Nominal values—confirm mill certificate.

Chemical Composition (%)

C0.17
NI1.5
CR0.35
MO0.2

Mechanical Properties

Tensile:≥1180 MPa;Yield:≥1080 MPa

Chinese Standard

DIN 17210 18CrNiMo5

Applications

高镍渗碳钢。,Bar

Available Forms

Carburizing (case-hardening) steel with low carbon core for toughness and a hard, wear-resistant surface after carburizing. Used for gears, camshafts, pinions, spline shafts, bushings and transmission parts subjected to fatigue and surface wear.

Uses

Typically normalized (880–920 °C, air cool) or carburized (900–930 °C) for case-hardening grades, then quenched and tempered at 150–200 °C. Carburize 900–930 °C, direct/intake quench, temper 150–200 °C; useful case depth 0.5–1.5 mm.

Heat Treatment

Weldable with standard procedures; preheat may be needed for thick sections or higher-carbon/ alloy grades. Protect from decarburization during heating (controlled atmosphere or protective coating). Machine the core stock before surface hardening; leave grinding allowance for the hardened case.

Precautions