20CrMo

Alloy Steel

20CrMo

Cr-Mo carburizing steel. (GB/T 3077; equiv GB 20CrMo / DIN 20CrMo4 / JIS SCM420). Nominal values—confirm mill certificate.

Chemical Composition (%)

C0.17
SI0.17
MN0.4
CR0.8
MO0.15
P0.035
S0.035

Mechanical Properties

Tensile:≥885 MPa;Yield:≥685 MPa;Elong:≥12%;RA:≥50%

Chinese Standard

T 3077 20CrMo

Equivalent Grades

GB 20CrMo / DIN 20CrMo4 / JIS SCM420

Applications

铬钼渗碳钢。,"Bar

Available Forms

Forging"

Uses

Carburizing (case-hardening) steel with low carbon core for toughness and a hard, wear-resistant surface after carburizing. Used for gears, camshafts, pinions, spline shafts, bushings and transmission parts subjected to fatigue and surface wear.

Heat Treatment

Typically normalized (880–920 °C, air cool) or carburized (900–930 °C) for case-hardening grades, then quenched and tempered at 150–200 °C. Carburize 900–930 °C, direct/intake quench, temper 150–200 °C; useful case depth 0.5–1.5 mm.

Precautions

Weldable with standard procedures; preheat may be needed for thick sections or higher-carbon/ alloy grades. Protect from decarburization during heating (controlled atmosphere or protective coating). Machine the core stock before surface hardening; leave grinding allowance for the hardened case.