4620H

Alloy Steel

4620H

Carburizing Ni-Cr-Mo steel. (ASTM A534; equiv GB 20CrNiMo / DIN 21NiCrMo2 / JIS SNCM220). Nominal values—confirm mill certificate.

Chemical Composition (%)

C0.18
SI0.15
MN0.7
NI0.4
CR0.4
MO0.15

Mechanical Properties

Tensile:≥640 MPa;Yield:≥420 MPa;Elong:≥18%

Chinese Standard

ASTM A534 4620H

Equivalent Grades

GB 20CrNiMo / DIN 21NiCrMo2 / JIS SNCM220

Applications

渗碳镍铬钼钢。,"Bar

Available Forms

Forging"

Uses

Carburizing (case-hardening) steel with low carbon core for toughness and a hard, wear-resistant surface after carburizing. Used for gears, camshafts, pinions, spline shafts, bushings and transmission parts subjected to fatigue and surface wear.

Heat Treatment

Typically normalized (880–920 °C, air cool) or carburized (900–930 °C) for case-hardening grades, then quenched and tempered at 150–200 °C. Carburize 900–930 °C, direct/intake quench, temper 150–200 °C; useful case depth 0.5–1.5 mm.

Precautions

Weldable with standard procedures; preheat may be needed for thick sections or higher-carbon/ alloy grades. Protect from decarburization during heating (controlled atmosphere or protective coating). Machine the core stock before surface hardening; leave grinding allowance for the hardened case.