4Cr9Si2
High-Temp Steel4Cr9Si2
Heat- and creep-resistant steel for elevated-temperature service with stable strength and oxidation resistance. Used in furnace parts, exhaust manifolds, turbine components, boiler tubes and engine va
Chemical Composition (%)
| C | 0.35 |
|---|---|
| SI | 2 |
| MN | 0.7 |
| CR | 8 |
| NI | 0.6 |
| P | 0.035 |
| S | 0.03 |
Applications
Heat- and creep-resistant steel for elevated-temperature service with stable strength and oxidation resistance. Used in furnace parts, exhaust manifolds, turbin
Available Forms
Bar, plate, forgings, tube
Uses
Heat- and creep-resistant steel for elevated-temperature service with stable strength and oxidation resistance. Used in furnace parts, exhaust manifolds, turbine components, boiler tubes and engine valves.
Heat Treatment
Normally used in the solution-annealed or precipitation-hardened condition; stabilise/age per the grade (e.g., 650–800 °C ageing). Avoid long exposure in the sigma/475 °C embrittlement ranges.
Precautions
Maintain the recommended heat-treatment envelope; prolonged time in embrittlement ranges reduces ductility. Use descaling/protective atmosphere to limit scaling.