65Si2MnWA
Alloy Steel65Si2MnWA
65Si2MnWA grade supplied by Shanxi Youte Steel (jlhsteel.net).
Chemical Composition (%)
| C | 0.61 |
|---|---|
| SI | 1.5 |
| MN | 0.7 |
| CR | 0.35 |
| CU | 0.2 |
| W | 0.8 |
Available Forms
Bar, Plate, Tube, Forging, Wire
Uses
Tool and die steel for cutting, forming, punching and molding tools. Tungsten/molybdenum (≈1%/0%) give hot hardness and red-hardness for high-speed and hot-work tools. High chromium (≈0.35%) provides wear resistance and secondary hardening. Applied to blanks, punches, extrusion dies, shear blades, plastic-mold and cold-work tooling.
Heat Treatment
Powder/HSS: preheat 800–850 °C, austenitize 1180–1230 °C (salt or vacuum), quench, triple temper 540–570 °C to ≈64–66 HRC.
Precautions
Risk of quench cracking and distortion — use graded preheating, controlled cooling and multiple tempers. Avoid overheating the austenitizing temperature. Machine in the soft annealed condition; allow for dimensional change after heat treatment. Grind with coolant to prevent rehardening cracks.