AH36

Alloy Steel

AH36

Specialty steel grade. tructural steel. (CCS A; equiv GL-AH36 / DH36 / EH36 / FH36). Nominal values—confirm mill certificate.

Chemical Composition (%)

C0.18
MN0.9
SI0.5
P0.035
S0.035

Mechanical Properties

Tensile:490-620 MPa;Yield:≥355 MPa

Equivalent Standards

GL-AH36 / DH36 / EH36

Applications

船体高强度结构钢。,Plate

Available Forms

Carburizing (case-hardening) steel with low carbon core for toughness and a hard, wear-resistant surface after carburizing. Used for gears, camshafts, pinions, spline shafts, bushings and transmission parts subjected to fatigue and surface wear.

Uses

Typically normalized (880–920 °C, air cool) or carburized (900–930 °C) for case-hardening grades, then quenched and tempered at 150–200 °C. Carburize 900–930 °C, direct/intake quench, temper 150–200 °C; useful case depth 0.5–1.5 mm.

Heat Treatment

Weldable with standard procedures; preheat may be needed for thick sections or higher-carbon/ alloy grades. Protect from decarburization during heating (controlled atmosphere or protective coating). Machine the core stock before surface hardening; leave grinding allowance for the hardened case.

Precautions

CCS A AH36 / FH36