AISI8620H

Alloy Steel

AISI8620H

Carburizing gear steel. (AISI/SAE; equiv 8620H). Nominal values—confirm mill certificate.

Chemical Composition (%)

C0.18
SI0.15
MN0.7
NI0.4
CR0.4
MO0.15

Mechanical Properties

Tensile:≥640 MPa;Yield:≥420 MPa;Elong:≥18%

Applications

渗碳镍铬钼钢。,Bar

Available Forms

Carburizing (case-hardening) steel with low carbon core for toughness and a hard, wear-resistant surface after carburizing. Used for gears, camshafts, pinions, spline shafts, bushings and transmission parts subjected to fatigue and surface wear.

Uses

Typically normalized (880–920 °C, air cool) or carburized (900–930 °C) for case-hardening grades, then quenched and tempered at 150–200 °C. Carburize 900–930 °C, direct/intake quench, temper 150–200 °C; useful case depth 0.5–1.5 mm.

Heat Treatment

Weldable with standard procedures; preheat may be needed for thick sections or higher-carbon/ alloy grades. Protect from decarburization during heating (controlled atmosphere or protective coating). Machine the core stock before surface hardening; leave grinding allowance for the hardened case.

Precautions

SAE AISI8620H / 8620H