ASP23
OtherASP23
PM high speed steel, equivalent to M3:2. High wear resistance & toughness.
Chemical Composition (%)
| C | 1.25 |
|---|---|
| W | 5 |
| MO | 4.5 |
| CR | 3.75 |
| V | 2.7 |
| P | 0.03 |
| S | 0.03 |
Mechanical Properties
Hardness(annealed):≤260 HB;Hardness(hardened):64-66 HRC
Chinese Standard
ASP23
Equivalent Grades
PM-M3:2 Grade
Applications
High wear hot/cold work, cutting tools, punches
Available Forms
Bar,Plate
Uses
Tool and die steel for cutting, forming, punching and molding tools. Tungsten/molybdenum (≈5.625%/4.875%) give hot hardness and red-hardness for high-speed and hot-work tools. High chromium (≈4.125%) provides wear resistance and secondary hardening. Applied to blanks, punches, extrusion dies, shear blades, plastic-mold and cold-work tooling.
Heat Treatment
Powder/HSS: preheat 800–850 °C, austenitize 1180–1230 °C (salt or vacuum), quench, triple temper 540–570 °C to ≈64–66 HRC.
Precautions
Risk of quench cracking and distortion — use graded preheating, controlled cooling and multiple tempers. Avoid overheating the austenitizing temperature. Machine in the soft annealed condition; allow for dimensional change after heat treatment. Grind with coolant to prevent rehardening cracks.