F6M
Stainless SteelF6M
Low-carbon martensitic, weldable & corrosion resistant. (ASTM A182; equiv ASTM A182 F6NM / JIS SCS6). Nominal values—confirm mill certificate.
Chemical Composition (%)
| C | 0.06 |
|---|---|
| CR | 11.5 |
| NI | 3.5 |
| MO | 0.4 |
Mechanical Properties
Tensile:≥760 MPa;Yield:≥550 MPa
Chinese Standard
ASTM A182 F6M
Equivalent Standards
ASTM A182 F6NM
Equivalent Grades
JIS SCS6
Applications
低碳马氏体，可焊耐蚀。,"Forging
Available Forms
Cast"
Uses
Ferritic stainless steel with good resistance to stress-corrosion cracking and oxidation, plus formability and lower cost. Used for automotive trim, exhaust systems, domestic appliances, decorative and welded structures.
Heat Treatment
Annealed at 780–850 °C and air cooled; stabilize at 600–800 °C to avoid 475 °C embrittlement; not hardenable by heat treatment.
Precautions
Avoid welding in the 475 °C embrittlement and sigma-phase ranges; use matched filler and minimize heat input. Good resistance to stress-corrosion cracking.