H22
OtherH22
Hot-work tool steel. (YB/T 5301; equiv ASTM A681 / DIN 1.2344 / JIS SKD61 / GB 4Cr5MoSiV1). Nominal values—confirm mill certificate.
Chemical Composition (%)
| C | 0.3 |
|---|---|
| CR | 1.75 |
| W | 10 |
| V | 0.25 |
| SI | 0.15 |
| MN | 0.15 |
| P | 0.03 |
| S | 0.03 |
Mechanical Properties
Hardness(annealed):≤235 HB;Hardness(hardened):46-54 HRC
Chinese Standard
T 5301 H22
Equivalent Standards
ASTM A681
Equivalent Grades
DIN 1.2344 / JIS SKD61 / GB 4Cr5MoSiV1
Applications
热作模具钢。,"Bar
Available Forms
Block"
Uses
Tool and die steel for cutting, forming, punching and molding tools. Tungsten/molybdenum (≈11%/0%) give hot hardness and red-hardness for high-speed and hot-work tools. High chromium (≈2.75%) provides wear resistance and secondary hardening. Applied to blanks, punches, extrusion dies, shear blades, plastic-mold and cold-work tooling.
Heat Treatment
Powder/HSS: preheat 800–850 °C, austenitize 1180–1230 °C (salt or vacuum), quench, triple temper 540–570 °C to ≈64–66 HRC.
Precautions
Risk of quench cracking and distortion — use graded preheating, controlled cooling and multiple tempers. Avoid overheating the austenitizing temperature. Machine in the soft annealed condition; allow for dimensional change after heat treatment. Grind with coolant to prevent rehardening cracks.