SSAB Hardox 400
OtherSSAB Hardox 400
Proprietary/trade-name steel grade SSAB Hardox 400
Chemical Composition (%)
| C | 0.2 |
|---|---|
| SI | 0.3 |
| MN | 0.8 |
| CR | 0.5 |
| NI | 0 |
| MO | 0.2 |
| B | 0 |
| P | 0.025 |
| S | 0.015 |
Applications
Manufacturer proprietary steel grade (trade name) per maker specification.
Available Forms
Bar, plate, sheet, tube, forgings, strip, wire, powder
Uses
Low-alloy engineering steel with enhanced hardenability and strength from alloying elements. Chromium (≈1.5%) improves hardenability, wear and corrosion resistance. Molybdenum (≈0.6%) raises high-temperature strength and prevents temper embrittlement. Nickel (≈1.25%) increases toughness and impact strength at low temperature. Applied to gears, shafts, bolts, connecting rods, pressure parts and heavy forgings in automotive, energy and machinery sectors.
Heat Treatment
Austenitize at 820–870 °C (oil or water quench depending on section) and temper at 400–650 °C to the required strength/toughness balance.
Precautions
Preheat and control interpass temperature when welding; post-weld heat treatment or stress relief is recommended to avoid hard-zone cracking. Use low-hydrogen electrodes. Protect from decarburization during heating (controlled atmosphere or protective coating).