VG10
VG10 · other
VG10
Round |
C:0.78-0.88;Si:0.20-0.45;Mn:0.15-0.40;Cr:3.75-4.50;Mo:4.50-5.50;W:5.50-6.75;V:1.75-2.20;P:≤0.030;S:≤0.030
Vica
Vicalloy 1 · alloy
Vicalloy 1
Bar,Rod,Powder |
Co:balance;Cr:28.0-32.0;W:3.5-5.5;C:1.0-1.4;Si:≤2.0;Mn:≤1.0;Fe:≤3.0
Vica
Vicalloy 2 · alloy
Vicalloy 2
Bar,Rod,Powder |
Co:balance;Cr:28.0-32.0;W:3.5-5.5;C:1.0-1.4;Si:≤2.0;Mn:≤1.0;Fe:≤3.0
W1
W1 · alloy
W1
Bar,Plate |
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
W10M
W10Mo4Cr4V3Co10 · other
W10Mo4Cr4V3Co10
Tool and die steel for cutting, forming, punching and molding tools. Tungsten/molybdenum (≈18.25%/0%) give hot hardness and red-hardness for high-speed and hot-work tools. High chromium (≈4.1%) provides wear resistance and secondary hardening. Applied to | T 9943 W10Mo4Cr4V3Co10
C:0.70-0.80;W:17.5-19.0;Cr:3.80-4.40;V:1.00-1.40
W12C
W12Cr4V5Co5 · other
W12Cr4V5Co5
Tool and die steel for cutting, forming, punching and molding tools. Tungsten/molybdenum (≈18.25%/0%) give hot hardness and red-hardness for high-speed and hot-work tools. High chromium (≈4.1%) provides wear resistance and secondary hardening. Applied to | T 9943 W12Cr4V5Co5
C:0.70-0.80;W:17.5-19.0;Cr:3.80-4.40;V:1.00-1.40
W12M
W12Mo3Cr4V3Co5Si · other
W12Mo3Cr4V3Co5Si
Tool and die steel for cutting, forming, punching and molding tools. Tungsten/molybdenum (≈18.25%/0%) give hot hardness and red-hardness for high-speed and hot-work tools. High chromium (≈4.1%) provides wear resistance and secondary hardening. Applied to | T 9943 W12Mo3Cr4V3Co5Si
C:0.70-0.80;W:17.5-19.0;Cr:3.80-4.40;V:1.00-1.40
W18C
W18Cr4V · other
W18Cr4V
Tool and die steel for cutting, forming, punching and molding tools. Tungsten/molybdenum (≈18.25%/0%) give hot hardness and red-hardness for high-speed and hot-work tools. High chromium (≈4.1%) provides wear resistance and secondary hardening. Applied to | T 1299 W18Cr4V
C:0.70-0.80;W:17.5-19.0;Cr:3.80-4.40;V:1.00-1.40;P:≤0.030;S:≤0.030
W2
W2 · alloy
W2
Bar,Plate |
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
W2Mo
W2Mo9Cr4V2 · other
W2Mo9Cr4V2
Tool and die steel for cutting, forming, punching and molding tools. Tungsten/molybdenum (≈6.125%/5%) give hot hardness and red-hardness for high-speed and hot-work tools. High chromium (≈4.1%) provides wear resistance and secondary hardening. Applied to | T 1299 W2Mo9Cr4V2
C:0.80-0.90;W:5.50-6.75;Mo:4.50-5.50;Cr:3.80-4.40;V:1.75-2.20
W2Mo
W2Mo9Cr4VCo8 · other
W2Mo9Cr4VCo8
Nickel/cobalt-base superalloy retaining high strength, creep and corrosion resistance at extreme temperature. Cobalt (≈8.25%) raises hot corrosion and wear resistance. Used in gas-turbine blades, aero-engine hot sections, combustors and advanced energy sy | T 9943 W2Mo9Cr4VCo8
C:1.05-1.15;W:1.15-1.85;Mo:9.00-10.00;Cr:3.50-4.25;V:0.95-1.15;Co:7.75-8.75;P:≤0.030;S:≤0.030
W3
W3 · alloy
W3
Bar,Plate |
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
W4
W4 · alloy
W4
Bar,Plate |
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
W4Mo
W4Mo3Cr4VSi · other
W4Mo3Cr4VSi
Tool and die steel for cutting, forming, punching and molding tools. Tungsten/molybdenum (≈6.125%/5%) give hot hardness and red-hardness for high-speed and hot-work tools. High chromium (≈4.1%) provides wear resistance and secondary hardening. Applied to | T 1299 W4Mo3Cr4VSi
C:0.80-0.90;W:5.50-6.75;Mo:4.50-5.50;Cr:3.80-4.40;V:1.75-2.20
W5
W5 · alloy
W5
Bar,Plate |
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
W68M
W68Mo5Cr4V2 · alloy
W68Mo5Cr4V2
Bar,Plate | T 588 W68Mo5Cr4V2
C:0.30-0.45;Mn:0.60-1.00;Si:0.15-0.35;Cr:0.50-1.00;P:≤0.035;S:≤0.040
W6Mo
W6Mo5Cr4V2 · other
W6Mo5Cr4V2
Tool and die steel for cutting, forming, punching and molding tools. Tungsten/molybdenum (≈6.125%/5%) give hot hardness and red-hardness for high-speed and hot-work tools. High chromium (≈4.1%) provides wear resistance and secondary hardening. Applied to | T 1299 W6Mo5Cr4V2
C:0.80-0.90;W:5.50-6.75;Mo:4.50-5.50;Cr:3.80-4.40;V:1.75-2.20;P:≤0.030;S:≤0.030
W6Mo
W6Mo5Cr4V2Al · other
W6Mo5Cr4V2Al
Tool and die steel for cutting, forming, punching and molding tools. Tungsten/molybdenum (≈6.125%/5%) give hot hardness and red-hardness for high-speed and hot-work tools. High chromium (≈4.1%) provides wear resistance and secondary hardening. Applied to | T 1299 W6Mo5Cr4V2Al
C:1.05-1.15;W:5.50-6.75;Mo:4.50-5.50;Cr:3.80-4.40;V:1.75-2.20;Al:0.80-1.20;P:≤0.030;S:≤0.030